Thin Film Coatings
A big part the value Janos Technology, LLC. provides is our offering of Thin Film Infrared Coatings and our ability to design a custom coating to meet your application needs. We start with our tried and true offering of infrared and mirror coatings. Janos Technology, LLC. has developed coatings that are available in wavelengths ranging from ultraviolet to the far infrared. Let our team deliver the assembly that has the coating to meet some of the toughest environments.
If you don’t see the product you are looking for, please Contact us, to see what we can to to support your program.
Janos Coatings:
Anti-Reflective (AR)
Hard Carbon (HCAR)
Multiple Band (BBAR)
Diamond-Like Carbon (DLC)
High Reflectance Metallic Coatings
| Type | Coating | Spectral Range | Substrate Material | Environmental Durability |
| string | string | string | string | string |
| Anti-Reflection (AR) | SWIR (Short Wave IR) | 0.8um – 2.5um | BaF2 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Anti-Reflection (AR) | SWIR (Short Wave IR) | 0.8um – 2.5um | CaF2 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Anti-Reflection (AR) | SWIR (Short Wave IR) | 0.8um – 2.5um | ZnSe | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Anti-Reflection (AR) | SWIR (Short Wave IR) | 0.8um – 2.5um | Cleartran | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Anti-Reflection (AR) | SWIR (Short Wave IR) | 0.8um – 2.5um | Fused Silica | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Anti-Reflection (AR) | SWIR/MWIR | 1.5um -5.0um | BaF2 | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-PRF-13830, Appendix c. |
| Anti-Reflection (AR) | SWIR/MWIR | 1.5um -5.0um | CaF2 | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-PRF-13830, Appendix c. |
| Anti-Reflection (AR) | SWIR/MWIR | 1.5um -5.0um | ZnSe | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-PRF-13830, Appendix c. |
| Anti-Reflection (AR) | SWIR/MWIR | 1.5um -5.0um | Cleartra | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-PRF-13830, Appendix c. |
| Anti-Reflection (AR) | SWIR/MWIR | 1.5um -5.0um | Silicon | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-PRF-13830, Appendix c. |
| Anti-Reflection (AR) | SWIR/MWIR | 1.5um -5.0um | Chalcogenide IRG22 | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-PRF-13830, Appendix c. |
| Anti-Reflection (AR) | SWIR/MWIR | 1.5um -5.0um | Chalcogenide IRG24 | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-PRF-13830, Appendix c. |
| Anti-Reflection (AR) | SWIR/MWIR | 1.5um -5.0um | Chalcogenide IRG25 | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-PRF-13830, Appendix c. |
| Anti-Reflection (AR) | SWIR/MWIR | 1.5um -5.0um | Chalcogenide IRG26 | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-PRF-13830, Appendix c. |
| Anti-Reflection (AR) | SWIR/MWIR | 1.5um -5.0um | AMTIR | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-PRF-13830, Appendix c. |
| Anti-Reflection (AR) | MWIR (Mid Wave IR) | 3.0um – 5.2um | BaF2 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Anti-Reflection (AR) | MWIR (Mid Wave IR) | 3.0um – 5.2um | CaF2 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Anti-Reflection (AR) | MWIR (Mid Wave IR) | 3.0um – 5.2um | ZnSe | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Anti-Reflection (AR) | MWIR (Mid Wave IR) | 3.0um – 5.2um | Silicon | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Anti-Reflection (AR) | MWIR (Mid Wave IR) | 3.0um – 5.2um | Chalcogenide IRG22 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Anti-Reflection (AR) | MWIR (Mid Wave IR) | 3.0um – 5.2um | Chalcogenide IRG24 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Anti-Reflection (AR) | MWIR (Mid Wave IR) | 3.0um – 5.2um | Chalcogenide IRG25 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Anti-Reflection (AR) | MWIR (Mid Wave IR) | 3.0um – 5.2um | Chalcogenide IRG26 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Anti-Reflection (AR) | MWIR (Mid Wave IR) | 3.0um – 5.2um | AMTIR | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Anti-Reflection (AR) | MWIR (Mid Wave IR) | 3.0um – 5.2um | Germanium | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Anti-Reflection (AR) | MWIR (Mid Wave IR) | 3.0um – 5.2um | GaAs | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Anti-Reflection (AR) | LWIR (Long Wave IR) | 7.5um – 13um | Germanium | Moderate abrasion, 24 hour humidity, Temperature test 2 hours each at -46 °C and +71 °C, and Adhesion per MIL-PRF-13830B, Appendix C |
| Anti-Reflection (AR) | LWIR (Long Wave IR) | 7.5um – 13um | AMTIR | Moderate abrasion, 24 hour humidity, Temperature test 2 hours each at -46 °C and +71 °C, and Adhesion per MIL-PRF-13830B, Appendix C |
| Anti-Reflection (AR) | LWIR (Long Wave IR) | 7.5um – 13um | GaAs | Moderate abrasion, 24 hour humidity, Temperature test 2 hours each at -46 °C and +71 °C, and Adhesion per MIL-PRF-13830B, Appendix C |
| Anti-Reflection (AR) | LWIR (Long Wave IR) | 7.5um – 13um | ZnS | Moderate abrasion, 24 hour humidity, Temperature test 2 hours each at -46 °C and +71 °C, and Adhesion per MIL-PRF-13830B, Appendix C |
| Anti-Reflection (AR) | LWIR (Long Wave IR) | 7.5um – 13um | ZnSe | Moderate abrasion, 24 hour humidity, Temperature test 2 hours each at -46 °C and +71 °C, and Adhesion per MIL-PRF-13830B, Appendix C |
| Anti-Reflection (AR) | LWIR (Long Wave IR) | 7.5um – 13um | Chalcogenide IRG22 | Moderate abrasion, 24 hour humidity, Temperature test 2 hours each at -46 °C and +71 °C, and Adhesion per MIL-PRF-13830B, Appendix C |
| Anti-Reflection (AR) | LWIR (Long Wave IR) | 7.5um – 13um | Chalcogenide IRG24 | Moderate abrasion, 24 hour humidity, Temperature test 2 hours each at -46 °C and +71 °C, and Adhesion per MIL-PRF-13830B, Appendix C |
| Anti-Reflection (AR) | LWIR (Long Wave IR) | 7.5um – 13um | Chalcogenide IRG25 | Moderate abrasion, 24 hour humidity, Temperature test 2 hours each at -46 °C and +71 °C, and Adhesion per MIL-PRF-13830B, Appendix C |
| Anti-Reflection (AR) | LWIR (Long Wave IR) | 7.5um – 13um | Chalcogenide IRG26 | Moderate abrasion, 24 hour humidity, Temperature test 2 hours each at -46 °C and +71 °C, and Adhesion per MIL-PRF-13830B, Appendix C |
| Dual Band | MWIR/LWIR | 3.5um 5.0um and 8um – 12um | BaF2 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | MWIR/LWIR | 3.5um 5.0um and 8um – 12um | CaF2 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | MWIR/LWIR | 3.5um 5.0um and 8um – 12um | ZnSe | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | MWIR/LWIR | 3.5um 5.0um and 8um – 12um | Cleartran | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | MWIR/LWIR | 3.5um 5.0um and 8um – 12um | Silicon | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | MWIR/LWIR | 3.5um 5.0um and 8um – 12um | Chalcogenide IRG22 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | MWIR/LWIR | 3.5um 5.0um and 8um – 12um | Chalcogenide IRG24 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | MWIR/LWIR | 3.5um 5.0um and 8um – 12um | Chalcogenide IRG25 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | MWIR/LWIR | 3.5um 5.0um and 8um – 12um | Chalcogenide IRG26 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | MWIR/LWIR | 3.5um 5.0um and 8um – 12um | AMTIR | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | MWIR/LWIR | 3.5um 5.0um and 8um – 12um | Germanium | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | MWIR/LWIR | 3.5um 5.0um and 8um – 12um | GaAs | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | MWIR/LWIR | 3.5um 5.0um and 8um – 12um | BaF2 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | MWIR/LWIR | 3.5um 5.0um and 8um – 12um | CaF2 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | MWIR/LWIR | 3.5um 5.0um and 8um – 12um | ZnSe | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | SWIR or MWIR/LWIR | Narrow pass band in SWIR (1.0um 2.5um) or MWIR (3.0um – (5.0um) and LWIR (8um – 12um) | Cleartran | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | SWIR or MWIR/LWIR | Narrow pass band in SWIR (1.0um 2.5um) or MWIR (3.0um – (5.0um) and LWIR (8um – 12um) | Silicon | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | SWIR or MWIR/LWIR | Narrow pass band in SWIR (1.0um 2.5um) or MWIR (3.0um – (5.0um) and LWIR (8um – 12um) | Chalcogenide IRG22 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | SWIR or MWIR/LWIR | Narrow pass band in SWIR (1.0um 2.5um) or MWIR (3.0um – (5.0um) and LWIR (8um – 12um) | Chalcogenide IRG24 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | SWIR or MWIR/LWIR | Narrow pass band in SWIR (1.0um 2.5um) or MWIR (3.0um – (5.0um) and LWIR (8um – 12um) | Chalcogenide IRG25 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | SWIR or MWIR/LWIR | Narrow pass band in SWIR (1.0um 2.5um) or MWIR (3.0um – (5.0um) and LWIR (8um – 12um) | Chalcogenide IRG26 | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | SWIR or MWIR/LWIR | Narrow pass band in SWIR (1.0um 2.5um) or MWIR (3.0um – (5.0um) and LWIR (8um – 12um) | Germanium | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Dual Band | SWIR or MWIR/LWIR | Narrow pass band in SWIR (1.0um 2.5um) or MWIR (3.0um – (5.0um) and LWIR (8um – 12um) | GaAs | Adhesion, Humidity Para. 4.5.3.2, Moderate Abrasion Para. 4.5.3.3, Adhesion Para. 4.5.3.1, Temerature Para. 4.5.4.1, Solubility and Cleanability Para. 4.5.4.2 per MIL-C-48497A |
| Diamond like Thin Film (DLC) | MWIR: DLC/AR | 3.0um – 5.2um | ZnSe | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | MWIR: DLC/AR | 3.0um – 5.2um | Cleartran | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | MWIR: DLC/AR | 3.0um – 5.2um | Silicon | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | MWIR: DLC/AR | 3.0um – 5.2um | AMTIR | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | MWIR: DLC/AR | 3.0um – 5.2um | Germanium | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | MWIR: DLC/AR | 3.0um – 5.2um | Aluminum | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | MWIR: DLC/AR | 3.0um – 5.2um | Stainless Steel | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | MWIR: DLC/AR | 3.0um – 5.2um | Chalcogenide IRG22 | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | MWIR: DLC/AR | 3.0um – 5.2um | Chalcogenide IRG24 | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | MWIR: DLC/AR | 3.0um – 5.2um | Chalcogenide IRG25 | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | MWIR: DLC/AR | 3.0um – 5.2um | Chalcogenide IRG26 | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | LWIR: DLC/AR | 7.5um – 13um | ZnSe | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | LWIR: DLC/AR | 7.5um – 13um | Cleartran | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | LWIR: DLC/AR | 7.5um – 13um | Silicon | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | LWIR: DLC/AR | 7.5um – 13um | Chalcogenide IRG22 | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | LWIR: DLC/AR | 7.5um – 13um | Chalcogenide IRG24 | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | LWIR: DLC/AR | 7.5um – 13um | Chalcogenide IRG25 | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | LWIR: DLC/AR | 7.5um – 13um | Chalcogenide IRG26 | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | LWIR: DLC/AR | 7.5um – 13um | AMTIR | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | LWIR: DLC/AR | 7.5um – 13um | Germanium | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | LWIR: DLC/AR | 7.5um – 13um | Aluminum | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | LWIR: DLC/AR | 7.5um – 13um | Stainless Steel | Temperature test 2 hours each at -46 °C and +71 °C, 10 Day humidity, 24 hour Salt Solubility, 48 hours Salt Spray per MIL-PRF-13830B, Appendix C and wiper Blade test (200 stroke severe abrasion test applies to Chalcogenide substrates instead of wiper blade test) |
| Diamond like Thin Film (DLC) | Protective DLC on Metals | N/A | Aluminum | High temereture, Lubricating film with low friction |
| Diamond like Thin Film (DLC) | Protective DLC on Metals | N/A | Stainless Steel | High temereture, Lubricating film with low friction |
| Diamond like Thin Film (DLC) | Protective DLC on Metals | N/A | Copper | High temereture, Lubricating film with low friction |
| Reflective (Mirror) | Protected UV Mirror | 0.25um – 0.75um and 2um – 14um | Aluminum | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Protected UV Mirror | 0.25um – 0.75um and 2um – 14um | Nickle | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Protected UV Mirror | 0.25um – 0.75um and 2um – 14um | Silicon | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Protected UV Mirror | 0.25um – 0.75um and 2um – 14um | Germanium | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Protected UV Mirror | 0.25um – 0.75um and 2um – 14um | any glass substrate | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Protected visible and IR Mirror | 0.4um – 0.7 um and 2um – 14um | Aluminum | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Protected visible and IR Mirror | 0.4um – 0.7 um and 2um – 14um | Nickle | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Protected visible and IR Mirror | 0.4um – 0.7 um and 2um – 14um | Silicon | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Protected visible and IR Mirror | 0.4um – 0.7 um and 2um – 14um | Germanium | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Protected visible and IR Mirror | 0.4um – 0.7 um and 2um – 14um | any glass substrate | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Enhanced Aluminum | 0.45um – 0.70um Higher reflection | Aluminum | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Enhanced Aluminum | 0.45um – 0.70um Higher reflection | Nickle | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Enhanced Aluminum | 0.45um – 0.70um Higher reflection | Silicon | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Enhanced Aluminum | 0.45um – 0.70um Higher reflection | Germanium | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Enhanced Aluminum | 0.45um – 0.70um Higher reflection | any glass substrate | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Durable Protected Gold | 0.8um – 14um | Aluminum | Adhesion, 24 Hour Humidity and Severe Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Durable Protected Gold | 0.8um – 14um | Nickle | Adhesion, 24 Hour Humidity and Severe Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Durable Protected Gold | 0.8um – 14um | Silicon | Adhesion, 24 Hour Humidity and Severe Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Durable Protected Gold | 0.8um – 14um | Germanium | Adhesion, 24 Hour Humidity and Severe Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Durable Protected Gold | 0.8um – 14um | any glass substrate | Adhesion, 24 Hour Humidity and Severe Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Unprotected Gold | 0.8um – 14um | any glass substrate | Adhesion |
| Reflective (Mirror) | Unprotected Gold | 0.8um – 14um | Aluminum | Adhesion |
| Reflective (Mirror) | Unprotected Gold | 0.8um – 14um | Nickle | Adhesion |
| Reflective (Mirror) | Unprotected Gold | 0.8um – 14um | Silicon | Adhesion |
| Reflective (Mirror) | Unprotected Gold | 0.8um – 14um | Germanium | Adhesion |
| Reflective (Mirror) | Enhanced Dielectric | 0.532um and 1.064um | any glass substrate | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Enhanced Dielectric | 0.532um and 1.064um | Aluminum | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Enhanced Dielectric | 0.532um and 1.064um | Nickle | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Enhanced Dielectric | 0.532um and 1.064um | Silicon | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Reflective (Mirror) | Enhanced Dielectric | 0.532um and 1.064um | Germanium | Adhesion, 24 Hour Humidity and Moderate Abrasion per MIL-C-48497A |
| Custom | Custom AR and Reflective | 0.25um – 15.0um | BaF2 | Per customer Specification |
| Custom | Custom AR and Reflective | 0.25um – 15.0um | CaF2 | Per customer Specification |
| Custom | Custom AR and Reflective | 0.25um – 15.0um | ZnSe | Per customer Specification |
| Custom | Custom AR and Reflective | 0.25um – 15.0um | Cleartra | Per customer Specification |
| Custom | Custom AR and Reflective | 0.25um – 15.0um | Fused Silica | Per customer Specification |
| Custom | Custom AR and Reflective | 0.25um – 15.0um | Silicon | Per customer Specification |
| Custom | Custom AR and Reflective | 0.25um – 15.0um | Chalcogenide IRG22 | Per customer Specification |
| Custom | Custom AR and Reflective | 0.25um – 15.0um | Chalcogenide IRG24 | Per customer Specification |
| Custom | Custom AR and Reflective | 0.25um – 15.0um | Chalcogenide IRG25 | Per customer Specification |
| Custom | Custom AR and Reflective | 0.25um – 15.0um | Chalcogenide IRG26 | Per customer Specification |
| Custom | Custom AR and Reflective | 0.25um – 15.0um | AMTIR | Per customer Specification |
| Custom | Custom AR and Reflective | 0.25um – 15.0um | Germanium | Per customer Specification |
| Custom | Custom AR and Reflective | 0.25um – 15.0um | Aluminum | Per customer Specification |
| Custom | Custom AR and Reflective | 0.25um – 15.0um | Stainless Steel | Per customer Specification |